Glass Ionomer Luting Cement

Glass Ionomer Luting Cement

The glass component is finely ground and sieved to produce an average particle size of less than 5 microns (<5μm).

This ensures a very low film thickness and excellent results in a host of procedures where cementation is required, especially for seating crowns and bridges.

FeaturesBenefits
Exceptional strength Long lasting cementations
Contains a high level of fluoride Helping prevent the build up of plaque
High wear and erosion resistance Durable Cementations
Easy mixing To reduce surgery time
Excellent biocompatibility Minimal pulpal reaction

 

Product indications

  • Cementing crowns and bridges
  • Cementing inlays and onlays
  • Orthodontic cementation of brackets and crowns
  • Base or lining material under composite, amalgam and glass ionomer filling material
  • Temporary filling material
  • Cementation of tooth jewellery

Typical properties

Working TimeNet Setting TimeCompressive StrengthLactic Acid ErosionFilm Thickness
ISO9917-1:2007 Class 4.2 a 1min 30secs (min) 1.5 mins – 8 mins 50MPa Minimum 0.17 mm/hr Maximum 25μm maximum
Glass Ionomer Luting Cement 3 mins 40 secs 3 mins 35 secs 122MPa 0.0068 mm/hr 17μm

 

Shelflife

Powder/Liquid (026X1): 3 years from the date of manufacture when supplied in AHL’s standard packaging.                        Powder/Liquid (259XPL): 3 years from the date of manufacture when supplied in AHL’s standard packaging.
Water Mix (081X2): 2 years from the date of manufacture when supplied in AHL’s standard packaging. 

Ordering information

Available inCode
30g Powder/15ml Liquid 026X1
Humid Stable 30g Powder/15ml Liquid 259XPL
Water Mix 15g 081X2 

 

More information about the product is available in Product Data Sheet here.